FR23 NA1000
Flame retardant ABS (non-PBBE additives). Good properties/toughness. Excellent moldability. UL94 V-0 rated.ASIAAMERICAS
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS | |
|---|---|---|---|---|
| MECHANICAL | ||||
| Tensile Stress, yld, Type I, 5 mm/min | 42 | MPa | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 35 | MPa | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 5 mm/min | 11 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 2410 | MPa | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 73 | MPa | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2720 | MPa | ASTM D 790 | |
| IMPACT | ||||
| Izod Impact, notched, 23°C | 267 | J/m | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 41 | J | ASTM D 3763 | |
| THERMAL | ||||
| Vicat Softening Temp, Rate B/50 | 90 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 83 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 72 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 7.92E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.92E-05 | 1/°C | ASTM E 831 | |
| Relative Temp Index, Elec | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B | |
| PHYSICAL | ||||
| Specific Gravity | 1.17 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm | 0.5-0.7 | % | SABIC method | |
| Melt Flow Rate, 230°C/3.8 kg | 6.8 | g/10 min | ASTM D 1238 | |
| Melt Viscosity, 200°C, 1000 sec-1 | 3100 | Poise | ASTM D 3825 | |
| Melt Flow Rate, 220°C/5.0 kg | 9 | g/10 min | ISO 1133 | |
| Melt Volume Rate, MVR at 220°C/10.0 kg | 37 | cm3/10 min | ISO 1133 | |
| FLAME CHARACTERISTICS | ||||
| UL Yellow Card | E207780-228348 | - | - | |
| UL Recognized, 94V-0 Flame Class Rating | 2.31 | mm | UL 94 | |
| UL Recognized, 94-5VB Flame Class Rating | 2.48 | mm | UL 94 |